Add to ORKGIn this report a rather comprehensive analysis is made of the frost and salt scaling resistance of concrete. Both theoretical and empirical information are provided. On that basis recommendations are given for the concrete quality that is required for a certain service life and also recommendations for testing of concrete with regard to its potential frost resistance
Concrete research is focusing ever more on the combined effect of degradation mechanisms on the dura...
A concrete submitted to freeze-thaw cycles may undergo damages generally identified under two forms....
A concrete submitted to freeze-thaw cycles may undergo damages generally identified under two forms....
A t.heory is presented for the estimation of the service life of concreLe Ðq)osed to frost action. I...
The purpose of this study is to summarize theoretical and practical knowledge of frost resistance of...
The report gives an overview of requirements and recommendations to frost durable concrete in standa...
Adequate measures must be taken during the determination of the concrete composition for ensuring th...
Adequate measures must be taken during the determination of the concrete composition for ensuring th...
Due to the variability of environmental loading, concrete is seldom subject to the effect of a singl...
AbstractUnder line Pathology of Materials; one of the environmental causes of damage effects on conc...
This study is based on determination of the freeze-thaw resistance of air-entrained and non-air-entr...
A theory is presented for the service life of concrete exposed to frost action. It is based on a sep...
Freeze-thaw tests and frost-salt tests were carried out for evaluating the frost resistance of F-con...
Concrete research is focusing ever more on the combined effect of degradation mechanisms on the dura...
Research on freeze-thaw resistance of concrete in general and on curing and moisture conditions in p...
Concrete research is focusing ever more on the combined effect of degradation mechanisms on the dura...
A concrete submitted to freeze-thaw cycles may undergo damages generally identified under two forms....
A concrete submitted to freeze-thaw cycles may undergo damages generally identified under two forms....
A t.heory is presented for the estimation of the service life of concreLe Ðq)osed to frost action. I...
The purpose of this study is to summarize theoretical and practical knowledge of frost resistance of...
The report gives an overview of requirements and recommendations to frost durable concrete in standa...
Adequate measures must be taken during the determination of the concrete composition for ensuring th...
Adequate measures must be taken during the determination of the concrete composition for ensuring th...
Due to the variability of environmental loading, concrete is seldom subject to the effect of a singl...
AbstractUnder line Pathology of Materials; one of the environmental causes of damage effects on conc...
This study is based on determination of the freeze-thaw resistance of air-entrained and non-air-entr...
A theory is presented for the service life of concrete exposed to frost action. It is based on a sep...
Freeze-thaw tests and frost-salt tests were carried out for evaluating the frost resistance of F-con...
Concrete research is focusing ever more on the combined effect of degradation mechanisms on the dura...
Research on freeze-thaw resistance of concrete in general and on curing and moisture conditions in p...
Concrete research is focusing ever more on the combined effect of degradation mechanisms on the dura...
A concrete submitted to freeze-thaw cycles may undergo damages generally identified under two forms....
A concrete submitted to freeze-thaw cycles may undergo damages generally identified under two forms....